RESEARCH
AND DEVELOPMENT WING - On Going and Recently Finished Development
|
|
|
Apart from regular improvement in
conventional Injection Moulded products through R&D we are
in a new field of Physical Cross Linking through E-Beam
Radiation Cross Linking Technology. Intensive R&D revealed a
remarkable improvement in physical & chemical properties in
the vulkazites of some polymer.
The reasons for improvement basically
were due to:
-
High Degree of Cross-Linking.
-
No polymer degradation due to high
temperature as EB Cross-linking occurs at room temperature
-
No oxidative degradation in
polymers as observed in chemical cross-linking
|
|
|
Present Status:
Development completed, Products are in field trial for
determination of actual service life
|
|
|
|
This high abrasion resistant metal bonded
pad used as a shim in coil springs under dynamic condition.
These pads are basically Thermoplastic & Millable
Polyurethane based. These prevents damage of spring under heavy
dynamic load. This also acts as a secondary suspension.
|
|
|
Present Status:
Development & Field Trial completed
|
|
|
|
External Rubber Jacket / Elastomeric
Membrane is suitable designed to protect from extreme weather
condition. The unique inside design enables prolonged service
life under heavy dynamic condition.
|
|
|
Present Status:
Development completed, Products are in extensive field trial for
determination of actual service life.
|
|
|
|
This product is designed to act as
suspension cum damper under heavy dynamic load and designed to
produce a very good service life. The polymer combination
used in this pad can resist high vertical, lateral & conical
load. It has almost zero chance of polymer cracking under
extreme weather condition and perfect for high speed wagons.
|
|
|
Present Status:
Designing completed, development & testing going on
|
|