ON GOING AND RECENTLY FINISHED DEVELOPMENT

ELECTRON BEAM RADIATED RINGS & SEALS

Apart from regular improvement in conventional Injection Moulded products through R&D we are in a new field of Physical Cross Linking through E-Beam Radiation Cross Linking Technology. Intensive R&D revealed a remarkable improvement in physical & chemical properties in the vulkazites of some polymer.

The reasons for improvement basically were due to:
  •  High Degree of Cross-Linking.
  • No polymer degradation due to high temperature as EB Cross-linking occurs at room temperature.
  • No oxidative degradation in polymers as observed in chemical cross-linking.

Present Status: Development completed, Products are in field trial for determination of actual service life

POLYURETHANE BASED SPRING PADS

This high abrasion resistant metal bonded pad used as a shim in coil springs under dynamic condition. These pads are basically Thermoplastic & Millable Polyurethane based. These prevents damage of spring under heavy dynamic load. This also acts as a secondary suspension.

Present Status: Development & Field Trial completed

RUBBER JACKETED ADAPTER BEARING PAD (HIGH-DYNAMIC ELASTOMERIC PAD)

External Rubber Jacket / Elastomeric Membrane is suitable designed to protect from extreme weather condition. The unique inside design enables prolonged service life under heavy dynamic condition.

Present Status: Development completed, Products are in extensive field trial for determination of actual service life.

POLYMERIC RING PAD FOR HIGH SPEED WAGON

This product is designed to act as suspension cum damper under heavy dynamic load and designed to produce a very good service life. The polymer combination used in this pad can resist high vertical, lateral & conical load. It has almost zero chance of polymer cracking under extreme weather condition and perfect for high speed wagons.

Present Status: Designing completed, development & testing going on.